Volume 39, No 1, 2017, Pages 100-109


Download full text in PDF

Effect of Shot Peening on Tribological Behaviors of Molybdenum-Thermal Spray Coating using HVOF Method

Authors:

H. Mohassel*, F. Malekabadi, M. Jebreili, M. Zehsaz,
F. Vakili-Tahami

DOI:10.24874/ti.2017.39.01.11

Abstract:

We have investigated the influence of post-shot peening on Mo-coating as compared to substrate steel 16MnCr5 (according to ZFN-413 A). Shot peening of carburized steel discs with and without Mo-coating was performed by using Shot size S230, Almen intensity 0.42 mm ’A’ and exposure time 96 sec. Tribological properties were analyzed, using pin-on-disc tribometer apparatus, under dry sliding conditions at different specific applied loads, sliding velocities and distance. Typical standardized methods were used for studying of surface integrity parameters (micro-hardness, topography and surface roughness). Surface morphology of the Mo-coating specimens with and without Shot Peening before and after wear was evaluated by Scanning Electron Microscopy. The results showed that shot peening after Mo-coating has considerable effect on improving wear resistance and because of having low friction coefficient has showed better wear behavior and tribologi cal properties over that of the un-peened Mo-coating.

Keywords:

Shot peening, Tribology, Molybdenum-Thermal Spray Coating, Almen Saturation Curve



Latest issue


tribology

Volume 46
Number 1
March 2024


Crossref logo




Announcements


TiI news RSS 2.0

Table of contents